Direct Formation of Thin-Walled Palladium Nanotubes in Nanochannels under an Electrical Potential
作 者 摘 要
In this work, we demonstrate a simple methodology for synthesizing vertical or free-standing palladium (Pd) nanotube arrays in a highly efficient fashion. The hydroxyl-terminated surface of the nanochannel in an alumina membrane is used to form an interfacial double layer by specifically adsorbing hydrogen ions (H+) from an acidic solution and leaving counterions to predominate in the diffuse layer. Locally enriched H+ ions at the wall of alumina nanochannel produce a higher content of adsorbed hydrogen on the electrochemically reduced metallic Pd surface under an appropriate electric potential. The higher Pd growth rate at peripheral positions rather than elsewhere in the nanochannel was due to the dual reductions of Pd(II) compound by hydrogen and electric potential. The disparity of growth rates in combination with diffusion-controlled growth efficiently gives rise to the formation of nanotubes with wall thicknesses as narrow as 6 nm.
详细资料 所属群组 标 签
相关链接
DOI URL
llcok_cn 的文献笔记 订阅 |
我最喜欢的一篇论文。
这个是我2011年发的第一篇论文，知识性很强，经过我大胆的设想和实验，最终轻松发了一篇不错的论文。 |
Electrochemical Growth of Silver Nanobelts in Cylindrical Alumina NanochannelsWet-Chemical Synthesis of Palladium Nanosprings
High-Yield Synthesis of Ultralong and Ultrathin Zn[sub:2]GeO[sub:4]Nanoribbons toward Improved Photocatalytic Reduction of CO[sub:2]into Renewable Hydrocarbon FuelBiosensing with plasmonic nanosensors
浙公网安备 33010202000686号 ( 浙ICP备09035230号-1 )
纳米材料化学